The Compleat
Sculptor " You supply the talent, we'll supply the rest!" Since 1995 |
EX-88 |
 |
||||||||||||||||
| EX-88 is an extremely clear, tough, high gloss surface coating formulated to produce a deep glass like appearance in a single layer on a sealed surface. EX-88 has an extended "open time" which allows up to 30 minutes in the mixing container at 70º F and up to one hour working time on the surface being coated. EX-88 is waterproof, heat & alcohol resistant. Used on restaurant table & bar tops for over 20 years. | |||||||||||||||||
Inquire About Larger Quantity Price Breaks |
|||||||||||||||||
| EX-88 is an excellent two-part epoxy coating for use on bar tops, tables and plaques. | ||||
A/B Mix Ratio: 1:1 |
Thin Film Set Time/Hour: 6 |
Durometer Hardness
2 Hours @ 60º C): 76 +/- 4 |
Tensile Strength: 2788 |
Tensile Modulus: 72,260 |
Tensile Elongation %: 64 |
Flexural Yield Strength: 1136 |
Flexural Yield Strain: 6.3 |
Flexural Yield Modulus: 56,511 |
Tg - ºC: 47 |
Viscosity CPS @ 77º F: Resin (A): 2400 Hardener (B): 1200 |
Density (lbs/gal): Resin (A): 9.61 Hardener (B): 8.01 |
VOC (grams/liter): 0 |
Gel Time (minutes) (100 gram
mass @ 22º C): 46 +/- 5 |
|
EX-74 |
 |
||||||||||||||||
| EX-74 is an extremely clear, tough, high gloss surface coating formulated to produce a deep glass like appearance in a single layer on a sealed surface. Two or more layers are often applied for added depth and protection. EX-74 has been formulated for improved UV resistance to reduce yellowing and surface degradation from UV exposure. EX-74 has an extended "open time" which allows up to 5 minutes in the mixing container at 70º F and up to one hour working time on the surface being coated. | |||||||||||||||||
Inquire About Larger Quantity Price Breaks |
|||||||||||||||||
| EX-74 is specially formulated to resist yellowing from exposure to sunlight. | ||||
A/B Mix Ratio: 1:1 |
Thin Film Set Time/Hour: 5 |
Durometer Hardness 2 Hours @ 60º C): 78 +/- 3 |
Tensile Strength: 3390 |
Tensile Modulus: 261,500 |
Tensile Elongation %: 24 |
Flexural Yield Strength: 6752 |
Flexural Yield Strain: 5.8 |
Flexural Yield Modulus: 197,848 |
Tg - ºC: 53 |
Viscosity CPS @ 77º F: Resin (A): 3500 Hardener (B): 1400 |
Density (lbs/gal): Resin (A): 9.64 Hardener (B): 8.05 |
VOC (grams/liter): 0 |
Gel Time (minutes) (100 gram mass @ 22º C): 51 +/- 3 |
|
|